Stoppani Plaster SIX

 
Characteristics

· Low specific weight
· Easy application (very good miscibility and detachment from the filler knife)
· Excellent elasticity
· Good vertical hold
· Good sanding
 
Specific weight: 0,57 ± 0,05 g/ml
Hardness shore D > 47
Pull-off adhesion ≥ 3.5 MPa

 
Substrate preparation
Stoppani epoxy primers
Dry sand with P280-320 paper

Application
Knifing.
Avoid applications at temperatures below 10°C and above 35°C.
At low temperatures avoid environments with high humidity, as the formation of a superficial sticky layer could make sanding difficult.

Mixing ratio
 
Volume
S26093 PLASTER SIX SOLUZIONE A .. ............................. 1000 ml
S26094 PLASTER SIX SOLUZIONE B ................................ 1000 ml

Maximum film thickness: 3,5 cm (35000 μ)
Recommended film thickness: not over 2 cm (20000 μ) per layer
Theoretical coverage A + B: 0,2 m2 for 1l at 0,5 cm (5000 μ) film thickness
Interval between coats: min. 24 h at 20°C
Solids content by volume: 100%
 
 
Drying  

 *The time of use is affected by the product volume prepared; larger quantities get warmer and have a shorter usage time. It is recommended to expand the product mass prepared, so as to increase its surface and to facilitate its cooling.

** At low temperatures the product has a higher viscosity; to make easier its workability, warm up the single components by a few minutes immersion in hot water before mixing.

TECHNICAL DATA SHEET N° S221-GB

UPDATED 02/2022

All information contained in this data sheet is the result of carefully controlled tests and is correct to the best of Lechler’s knowledge at the time of issue. Since conditions of use are beyond the control of the manufacturer, information contained herein is without warranty, implied or otherwise, and final determination of the suitability of any information or material for the use contemplated and the manner of use is the sole responsibility of the user. FOR PROFESSIONAL USE ONLY.