2K high build epoxy primer. Used for hull protection in paint processes on steel, aluminium and gelcoat boats. It offers a very good barrier to water and it can be used on the ship’s bottom (under the waterline) as well as on topside (above the waterline). Especially suitable to insulate the filler, it allows to obtain a high protection level with a limited number of coats. On fibreglass boats it avoids osmosis formation and it favours antifouling adhesion.
Yachting | Fibreglass | Steel | Aluminium | Primers and undercoats | Two-pack | Aerosols | Brush/roller |
 |
 |
| 1000/250 ml | Ø 1,5-1,9 mm 3,5-4 Atm HVLP: 2-2,5 Atm N° coats:2 |
 |
 |
| 1h at 20°C | 180-220μ |
 |
 |
| 24h at 20°C | 2.3 m2/l at 200μ dry film thickness |
S2402. EPOXY HIGH PROTECTION
Colour
S24020 White
S24021 Grey
Characteristics
· Very good filling power
· Very good overcoating without sanding
· High vertical stability
· Very good impermeability
Specific weight (part A): 1,65 ± 0,05 g/ml
Specific weight (part B): 0,91 ± 0,05 g/ml
Substrate preparation
Steel
Sanding disc Sa 2,5
Aluminium, light alloys
Sand blasting, disc sanding P-36
Gelcoat
Dry sanding with P120-180 abrasive paper Lechler S.p.A. 22100 COMO ITALY - Via Cecilio, 17 Tel. +39.031 586 111 - Fax +39.031 586 206 info@lechler.eu www.lechler.eu
2K epoxy primers Stoppani
Sand dry with P240-280 abrasive paper
2K epoxy fillers Stoppani
Sand dry with P180-220 abrasive paper
Application
Airless or spray with traditional spray gun or HVLP, by brush or roller.
Application conditions:
Relative humidity < 80%
Spray temperature >10 °C <35°C
Substrate temperature 5 °C >dew point
Mixing ratio
Conventional Spray
| volume | weight | |
| S24020-21 EPOXY HIGH PROTECTION .A | 1000 ml | 1000 g |
| S24022 EPOXY HIGH PROTECTION HARDENER B | 250 ml | 140 g |
| S70171-00535 EPOXY THINNER C | 100-250 ml | 50-125 g |
Airless/Roller
| volume | weight | |
| S24020-21 EPOXY HIGH PROTECTION .A | 1000 ml | 1000 g |
| S24022 EPOXY HIGH PROTECTION HARDENER B | 250 ml | 140 g |
| S70171-00535 EPOXY THINNER C | 0-100 ml | 0-50 g |
Pot life at 20°C: 3h
N° of coats: 2
Recommended film thickness: 180-220μ dry (2 coats by spray of 200μ wet each)
Minimum interval between coats: 24 h by roller or brush,1h by spray at 20°C
Airless/Roller
Air cap 0.3-0.38 mm, pressure 80-150 Bars
Solids content by volume mix A+B+C by spray Airless: 51.1 %
Theoretical coverage mix A+B+C by spray Airless: 2.6 m2 for 1l mixture at 200μ film thickness
Conventional Spray
Ø conventional air cap and HVLP 1,7-1.9 mm
Pressure: 3,5 – 4 Atm HVLP: 2 – 2,5 Atm
Solids content by volume mix A+B+C by conventional spray: 46.1 %
Theoretical coverage mix A+B+C by conventional spray: 2.3 m2 for 1l mixture at 200μ film thickness
Drying
| 10°C | 20°C | 35°C | |
|
Sanding after |
48 h |
24 h |
12 h |
|
Overcoat with itself by brush or roller |
min. 48 h max 30 days |
min. 24 h max 30 days |
min. 12 h max 30 days |
|
Overcoat with itself by spray |
min. 2h max 30 days |
min. 1h max 30 days |
min. 30’ max 30 days |
|
Overcoat with Filler Epox |
min. 32h max 30 days |
min. 16h max 30 days |
min. 8h max 30 days |
Thinner for spray application of 1K topcoats, fillers, primers, clearcoats and polyurethane enamels. Due to the high costs of international ADR shipments (dangerous goods), this product is available as standard only in Italy. However, if you want you can ask for a quote...
Epoxy thinner for the spray and brush application of epoxy products.
1K anticorrosive primer based on modified alkyd resins. It contains active anticorrosive pigments for iron protection and is suitable as rot-proof wood impregnating agent. It can be used both on the ships bottom (under the waterline) and on upper works (above the waterline). Wood | Steel | Primers and undercoats | Mono-composant | Aerosols |...
1K universal primer and intermediate coat formulated with resins based on chlorinated rubber and aluminium pigments. It can be used both on the ships bottom (under the waterline) and as an adherence coat between antifouling products in careening operations or in order to help the antifouling adherence to dried epoxy primers. Wood | Fibreglass | Steel |...
2K epoxy primer. Used for hull protection in the paint processes on steel, wood, zinc-coated steel and gelcoat boats. It can be used on the ships bottom (under the waterline) as well as on topside ( above the waterline). On fibreglass boats it avoids osmosis formation and helps antifouling adhesion. Wood | Fibreglass | Steel | Aluminium | Primers and...
2K hi-build epoxy filler undercoat. Especially suitable for paint processes where epoxy putty sealing is essential. It can be used above the waterline (upper works). Wood | Fibreglass | Steel | Aluminium | Primers and undercoats | Two-pack | Aerosols | Brush/roller | Above the waterline |
1K synthetic undercoat formulated with glyceryl phthalate resins. It can be used above the waterline (upper works), applicable over knifing putties or anticorrosive primers before the topcoats. This product can be over coated only with 1K products.
2K black epoxy coating with a high film thickness. Suitable for metal and concrete surfaces subjected to total immersion in water. Suitable for the yachting field, for painting under the waterline (ships bottom). Steel | Aluminium | Primers and undercoats | Two-pack | Aerosols | Brush/roller | Under the waterline |
2K sealing undercoat for dry-on-dry paint processes formulated with polyester resin. Suitable as an undercoat for finishing enamels in the yachting field, to seal and fill surfaces with different degrees of absorption. It can also be used as sealer on epoxy primers, before the topcoat, above the waterline (upper works). Wood | Fibreglass | Steel |...
2K high build epoxy primer. Used for hull protection in paint processes on steel, aluminium and gelcoat boats. It offers a very good barrier to water and it can be used on the ship’s bottom (under the waterline) as well as on topside (above the waterline). Especially suitable to insulate the filler, it allows to obtain a high protection level with a limited number of coats. On fibreglass boats it avoids osmosis formation and it favours antifouling adhesion.
Yachting | Fibreglass | Steel | Aluminium | Primers and undercoats | Two-pack | Aerosols | Brush/roller |
Crispy 520 on the water
Simple Guide to Epoxies
Idea 850 in Poland