Colour
Available in the following colours: S74155 white; S74157 red and S74158 grey
Characteristics
· Very fast drying
· Multipurpose application.
· Very good adhesion
· Good sanding.
Specific weight (part A): 1,35 ± 0,05 g/ml
Specific weight (part B): 0,97 ± 0,03 g/ml
Substrate preparation
Steel
Sanding disc Sa 2,5
Gelcoat
Dry sanding with P120-180 paper
Wood
Sanding with P120 paper
Zinc-coated steel
Rub down with red scotchbrite
Aluminium, light alloys
Sand blasting, disc sanding P-36
Application
By brush, roller, airless and spray with traditional spray gun or HVLP.
Relative humidity < 80%
Spray temperature >10 °C <35°C
Substrate temperature 5 °C >dew point
Mixing ratio
Brush or roller |
volume |
weight |
EPOXY PLUS A |
900 ml |
925 g |
HARDENER B |
100 ml |
75 g |
EPOXY THINNER C |
100-150 ml |
50-100 g |
Spray or airless |
volume |
weight |
EPOXY PLUS A |
900 ml |
925 g |
HARDENER B |
100 ml |
75 g |
EPOXY THINNER C |
150-250 ml |
100-150 g |
Pot life at 20°C: 7h
Ø conventional spray gun and HVLP 1,5-1,9 mm
Pressure: 3,5 – 4 Atm HVLP: 2 – 2,5 Atm
N° of coats: 1-5
Recommended film thickness as anticorrosive paint :50 - 70ì dry (n°2 coats by spray of 80 ì wet each)
Recommended film thickness as antiosmosis paint: 200-250 ì (n°5 coats by roller of 110 ì wet each)
Interval between coats: 16 h by roller/brush, 60’ by spray
Theoretical coverage A+B : 7,5 m2 for 1l at 60 ì film thickness
Theoretical coverage A+B+C : 6,4 m2 for 1l at 60 ì film thickness
Solids content by volume A+B: 45,2 %
Solids content by volume A + B + C by spray: 38,1%
Drying
|
10°C |
20°C |
35°C |
Sanding after
|
32 h |
16 h |
8 h |
Overcoat with Epoxy Plus
|
min. 2 h max. 96 h |
min. 1 h max. 48 h |
min. 30’ max. 24 h |
Overcoat with epoxy Filler
|
min. 16 h max. 96 h |
min. 8 h max. 48 h |
min. 4 h max. 24 h |
Overcoat with Undercoat PU
|
min. 16 h max. 96 h |
min. 8 h max. 48 h |
min. 4 h max. 24 h |
Overcoat with Antifouling
|
min. 16 h max. 96 h |
min. 8 h max. 48 h |
min. 4 h max. 24 h |